Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
Product Feature
- Good Mechanical Properties: Our composite materials exhibit excellent mechanical properties, ensuring durability and reliability in various conditions.
- Electrical Insulation: With superior electrical insulation, our product provides a safe and reliable solution for electrical applications.
- Arc Resistance and Anti-Static: Our materials are specifically engineered to resist arcs and prevent static buildup, making them ideal for applications where safety is paramount.
- Corrosion Resistance: Our composites offer exceptional resistance to corrosion, including acid and alkali solutions, ensuring longevity and reliability in harsh environments.
- Lightweight and High Product Utilization: Our materials are lightweight, allowing for easy handling and transportation. Additionally, their high product utilization ensures maximum efficiency and cost-effectiveness.
- Strong Designability: Our composites offer great design flexibility, allowing for the creation of custom-made products that meet specific requirements.
- Widely Used: Our composite materials find extensive use in various industries, making them a versatile solution for a wide range of applications.
Product Parameters
| NO. |
Test ltem |
Unit |
Index |
Test |
| 1 |
Resin Content |
% |
Customized |
39 |
| 2 |
Volatile Matter Content |
% |
4.0-8.5 |
6 |
| 3 |
Density |
g/cm3 |
1.65-1.85 |
1.85 |
| 4 |
Moisture Content |
mg |
≤20 |
18 |
| 5 |
Martens Temperature |
ºC |
≥280 |
280 |
| 6 |
Bending Strength |
Mpa |
≥160 |
415 |
| 7 |
Tensile Strength |
Mpa |
≥80 |
160 |
| 8 |
Dielectric Strength |
MV/m |
≥14.0 |
18 |
| 9 |
Charpy Impact Strength |
KJ/m2 |
≥50 |
120 |
| 10 |
Surface Resistivity |
Ω |
≥1.0x10^12 |
2.0*10^13 |
| 11 |
Volume Resistivity |
Ω.m |
≥1.0x10^10 |
2.6*10^12 |
| 12 |
Flexural Modulus |
Gpa |
32.4 |
33 |
Application
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
Packaging & Shipping
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015