| Customization: | Available |
|---|---|
| Certification: | CE |
| Technique: | Winding Filament Roving |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Our White S-Glass Fabric is a high-strength glass fiber product that is specifically designed for marine applications.With over 30-40% higher tensile strength and 16-20% higher modulus of elasticity compared to E Glass fiber, our S-Glass Fabric offers superior performance.
Not only does our S-Glass Fabric have 10 times higher fatigue resistance, but it can also endure temperatures that are 100-150 degrees higher than E Glass fiber. Its excellent impact resistance is due to its high elongation to break, as well as its high aging and corrosion resistance. Additionally, our S-Glass Fabric has quick resin wet-out properties, making it easy to work with.
Aerospace, marine, and arms industries benefit from the high tensile strength and modulus of elasticity of our White S-Glass Fabric. Perfect for marine applications, our top-quality S-Glass Roving offers durability and exceptional performance.
|
Data Sheet of S-Glass & E-Glass |
||
|
Properties |
S-Glass |
E-Glass |
|
Virgin Fiber Tensile Strength(Mpa) |
4100 |
3140 |
|
Tensile Strength(Mpa) ASTM 2343 |
3100-3600 |
1800-2400 |
|
Tensile Modulus(Gpa) ASTM 2343 |
82-86 |
69-76 |
|
Elongation To Break(%) |
4.9 |
4.8 |
|
Properties |
BH-HS2 |
BH-HS4 |
E-glass |
|
Virgin fiber tensile strength(Mpa) |
4100 |
4600 |
3140 |
|
Tensi1e strength(MPA) ASTM2343 |
3100-3600 |
3300-4000 |
1800-2400 |
|
Tensile Modulus (GPa)ASTM2343 |
82-86 |
83-90 |
69-76 |
|
Elongation to break(%) |
49 |
54 |
48 |