Product Description
Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
Product Feature
- Good Mechanical Properties: Our products exhibit excellent mechanical properties, ensuring durability and long-lasting performance.
- Electrical Insulation: With superior electrical insulation, our products provide a safe and reliable solution for various applications.
- Arc Resistance and Anti-Static: Designed to withstand arc and static electricity, our products offer enhanced safety and protection.
- Good Corrosion Resistance: Our products are highly resistant to corrosion, making them suitable for use in acidic, alkaline, and other chemical environments.
- Lightweight and High Product Utilization: Weighing less and offering high product utilization, our products are convenient to use and maximize efficiency.
- Strong Designability: Our products provide flexibility in design, allowing for customization and meeting specific requirements.
- Widely Used: Our products find extensive applications across various industries due to their versatile nature and reliable performance.
Product Parameters
| NO. |
Test ltem |
Unit |
Index |
Test |
| 1 |
Resin Content |
% |
Customized |
38 |
| 2 |
Volatile Matter Content |
% |
3.0-6.0 |
3 |
| 3 |
Density |
g/cm3 |
1.65-1.85 |
1.85 |
| 4 |
Moisture Content |
mg |
≤20 |
20 |
| 5 |
Martens Temperature |
ºC |
≥280 |
280 |
| 6 |
Bending Strength |
Mpa |
≥450 |
716 |
| 7 |
Charpy Impact Strength |
KJ/m2 |
≥180 |
211 |
| 8 |
Tensile Strength |
Mpa |
≥300 |
315 |
| 9 |
Surface Resistivity |
Ω |
≥1.0x10^12 |
6.3x10^12 |
| 10 |
Volume Resistivity |
Ω.m |
≥1.0x10^10 |
2.8x10^10 |
| 11 |
Dielectric loss factor |
- |
≤0.04 |
0.04 |
| 12 |
Relative dielectric constant |
- |
≤7 |
6 |
| 13 |
Dielectric Strength |
MV/m |
≥14.0 |
14.5 |
| 14 |
Flexural Modulus |
Gpa |
32 |
33 |
Application
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
Packaging & Shipping
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015