Product Description
Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
Product Feature
- Good Mechanical Properties: Our composite material exhibits excellent mechanical properties, ensuring durability and reliability.
- Electrical Insulation and Arc Resistance: With superior electrical insulation and arc resistance, our product guarantees safe and efficient performance.
- Anti-Static: Our composite material is anti-static, preventing the buildup of static electricity and reducing the risk of damage to sensitive equipment.
- Good Corrosion Resistance: Our product is highly resistant to corrosion, making it suitable for use in various environments, including exposure to acid and alkali solutions.
- Lightweight and High Product Utilization: Our composite material is lightweight, allowing for easy handling and transportation. It also offers high product utilization, maximizing its efficiency and cost-effectiveness.
- Strong Designability: Our product provides excellent design flexibility, enabling it to be used in a wide range of applications.
- Widely Used: Our composite material finds extensive use in various industries due to its exceptional properties and versatility.
Product Parameters
| NO. |
Test ltem |
Unit |
Index |
Test |
| 1 |
Resin Content |
% |
Customized |
38 |
| 2 |
Volatile Matter Content |
% |
3.0-6.0 |
3 |
| 3 |
Density |
g/cm3 |
1.65-1.85 |
1.85 |
| 4 |
Moisture Content |
mg |
≤20 |
20 |
| 5 |
Martens Temperature |
ºC |
≥280 |
280 |
| 6 |
Bending Strength |
Mpa |
≥450 |
716 |
| 7 |
Charpy Impact Strength |
KJ/m2 |
≥180 |
211 |
| 8 |
Tensile Strength |
Mpa |
≥300 |
315 |
| 9 |
Surface Resistivity |
Ω |
≥1.0x10^12 |
6.3x10^12 |
| 10 |
Volume Resistivity |
Ω.m |
≥1.0x10^10 |
2.8x10^10 |
| 11 |
Dielectric loss factor |
- |
≤0.04 |
0.04 |
| 12 |
Relative dielectric constant |
- |
≤7 |
6 |
| 13 |
Dielectric Strength |
MV/m |
≥14.0 |
14.5 |
| 14 |
Flexural Modulus |
Gpa |
32 |
33 |
Application
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
Packaging & Shipping
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015