| Customization: | Available |
|---|---|
| Certification: | CE |
| Technique: | Winding Filament Roving |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Compared to E Glass fiber, our S Glass Yarn offers some amazing advantages. It boasts 30-40% higher tensile strength, 16-20% higher modulus of elasticity, and an impressive 10 times higher fatigue resistance. Not only that, but it can endure temperatures 100-150 degrees higher than other fibers, making it ideal for demanding environments. Plus, its high elongation to break ensures excellent impact resistance.
But that's not all! Our S Glass Yarn also possesses exceptional aging and corrosion resistance, as well as quick resin wet-out properties. It's truly a top-quality product that meets the needs of the aerospace and marine industries.
S-Glass Yarn for the aerospace and marine industries. Our S-Glass Yarn has exceptional tensile strength and elasticity, making it ideal for applications in aerospace and marine sectors. Choose our top-quality S-Glass Yarn for durable and reliable performance.
|
Data Sheet of S-Glass & E-Glass |
||
|
Properties |
S-Glass |
E-Glass |
|
Virgin Fiber Tensile Strength(Mpa) |
4100 |
3140 |
|
Tensile Strength(Mpa) ASTM 2343 |
3100-3600 |
1800-2400 |
|
Tensile Modulus(Gpa) ASTM 2343 |
82-86 |
69-76 |
|
Elongation To Break(%) |
4.9 |
4.8 |
|
Properties |
BH-HS2 |
BH-HS4 |
E-glass |
|
Virgin fiber tensile strength(Mpa) |
4100 |
4600 |
3140 |
|
Tensi1e strength(MPA) ASTM2343 |
3100-3600 |
3300-4000 |
1800-2400 |
|
Tensile Modulus (GPa)ASTM2343 |
82-86 |
83-90 |
69-76 |
|
Elongation to break(%) |
49 |
54 |
48 |