| Customization: | Available |
|---|---|
| Certification: | CE |
| Technique: | Winding Filament Roving |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Made from high-strength glass fibers derived from the magnesium alumino silicate glass system, this fabric surpasses the performance of E Glass fiber.
With 30-40% higher tensile strength and 16-20% higher modulus of elasticity compared to E Glass fiber, our S-Glass Fiber Fabric ensures superior performance in demanding conditions. It also boasts 10 times higher fatigue resistance and can endure temperatures 100-150 degrees higher. Its excellent impact resistance, thanks to its high elongation to break, makes it an ideal choice for arms applications.
In addition to its impressive strength and endurance, our S-Glass Fiber Fabric exhibits high ageing and corrosion resistance. Its quick resin wet-out properties make it easy to work with, ensuring efficient production processes.
Aerospace, marine and arms industries due to its high tensile strength and higher modulus of elasticity when compared to e-glass.
|
Data Sheet of S-Glass & E-Glass |
||
|
Properties |
S-Glass |
E-Glass |
|
Virgin Fiber Tensile Strength(Mpa) |
4100 |
3140 |
|
Tensile Strength(Mpa) ASTM 2343 |
3100-3600 |
1800-2400 |
|
Tensile Modulus(Gpa) ASTM 2343 |
82-86 |
69-76 |
|
Elongation To Break(%) |
4.9 |
4.8 |
|
Properties |
BH-HS2 |
BH-HS4 |
E-glass |
|
Virgin fiber tensile strength(Mpa) |
4100 |
4600 |
3140 |
|
Tensi1e strength(MPA) ASTM2343 |
3100-3600 |
3300-4000 |
1800-2400 |
|
Tensile Modulus (GPa)ASTM2343 |
82-86 |
83-90 |
69-76 |
|
Elongation to break(%) |
49 |
54 |
48 |